End Cap 2:1 Shrink Ratio

WRSFM Crosslinked Polyolefin End Cap

Heat shrink end caps are a simple yet effective method for sealing cable ends, pipe conduit or other similar objects.

2:1 shrink ratio

Superior resistance to weathering

Resistant to common fluids and standard adhesive liner provides coated hot melt adhesive resists

Continuous operating temperature: (value not specified)

Shrink temperature: 120°C

Dimensions & Packaging

As supplied and after recovery dimensions (values as per datasheet)

Part No.	Inner diameter (mm)		Full length (mm)	Wall thickness (mm)
	As supplied (min)	After recovery (max)		As supplied	After recovery (min)
WRSFM-11/5	≥11	≤5.5	≥22	------	≥1.1
WRSFM-16/7	≥16	≤7.5	≥75	1.3±0.1	≥2.2
WRSFM-25/10	≥25	≤10.5	≥80	1.5±0.1	≥2.3
WRSFM-32/16	≥32	≤16.5	≥90	1.5±0.1	≥2.5
WRSFM-50/26	≥50	≤26	≥115	2.0±0.1	≥3.4
WRSFM-70/37	≥70	≤30	≥125	1.8±0.1	≥2.5
WRSFM-100/46	≥100	≤40	≥140	1.8±0.1	≥3.5
WRSFM-120/57	≥120	≤57	≥155	1.8±0.1	≥3.5

*Other sizes are available upon request.

Physical, electrical and environmental properties

知

Property	Test Method	Standard Value
Tensile strength (MPa)	ASTM D2671	≥13
Elongation (%)	ASTM D2671	≥300
Tensile strength after thermal aging (MPa)	ASTM D2671 (120°C/168h)	≥11
Elongation after thermal aging (%)	ASTM D2671 (120°C/168h)	≥210
Longitudinal shrinkage (%)	UL 224	≤10
Eccentricity (%)	ASTM D2671	＜30
Water absorption (%)	ISO 62	≤0.1
Volume resistance (Ω·cm)	IEC 93	≥1×10¹⁴
Dielectric strength (kV/mm)	IEC 243	≥20
Resistance to stress cracking	ASTM D1693 (50°C)	No cracking
Resistance to fungus and decay	ISO 846	Pass

← swipe →

Suitable for sealing cable ends, pipes and conduits.